Surface Modification of Natural Graphite by Phenolic Resin Carbon Coating for Improvement of Cyclic Performances in Lithium Ion Batteries

注意：本论文已在Energy Sources, 25:827–836, 2003发表
使用者请注明论文出处
BAOHUA LI,KAIXI LI,YONGGEN LU,CHUNXIANG LU,LICHENG LING
State Key Laboratory of Coal Conversion
Institute of Coal Chemistry
Chinese Academy of Sciences
Taiyuan, Shanxi, People’s Republic of China

Abstract:Natural graphite was coated with different concentrations of phenolic resin and methane solution. To obtain modified graphite, the coated natural graphite was further carbonized at a temperature of 1000℃ for 1 hunder a N2 stream after removing the solvent of methane. The surface morphology and microstructure of modified graphite were investigated with scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. Thecomputer-controlled constant-current cycler investigated charge and discharge performances. Results showed that the phenolic resin carbon with disordered structure formed on the surface of graphite could protect the graphite from exfoliation and improve its cyclic performances successfully. The reversible capacity and coulombic efficiencies of modified graphite were higher than that of natural graphite during charge and discharge cycling tests at a rate of 50mA · g-1. It is confirmed that modified graphite has an advantage for an application of high power density lithiumion battery.
Keywords: natural graphite, lithium ion battery, carbon anode, phenolic resin

1、浏览PDF格式全文需要使用软件－－Abode Acrobat(由于软件较大并常见,我站不提供下载)

2、下载论文全文请点击鼠标右键“另存为”或使用断点续传软件下载(1,068KB)

1、Preparation of Porous Carbon Microspheres

2、Preparation of mesocarbon microbeads from coal tar

3、用称重法研究聚丙烯腈树脂的凝固过程

4、掺磷酚醛树脂炭嵌锂性能研究

5、聚丙烯腈纤维在预氧化过程中的结构和热性能转变

6、中间相沥青碳微球的制备及其嵌锂行为的研究

　更多相关论文请点击本站的<<<站内全文搜索>>>查找

>>>>参加更多投票调查请点击！