Preparation of Porous Carbon Microspheres

注意:本论文已在 Inc. J Appl Polym Sci 102:798–803, 2006发表
使用者请注明论文出处

Yonggen Lu(吕永根),1 Changling Yang,2 Haiqin Rong,1 Ding Pan1
1Department of Composite Material and Engineering, College of Material Sciences and Engineering, Donghua
University, Shanghai 200051, China
2Department of Basic Chemistry, College of Chemistry and Chemical Engineering, Donghua University, Shanghai
200051, China

Abstract: Porous carbon microspheres with good morphology, high yield, and controllable particle size were prepared from phenolic resin. The particle size and pore structure
of the carbon microspheres were mainly inherited from their precursors, resol microspheres, which were made through curing emulsified resol in water at 120°C under saturated pressure. The average particle size and specific surface area of the porous carbon microspheres was related to the concentration of resol and polyvinyl alcohol along with the heating program. The carbonization yield to 700°C was 55 wt %.
Keyword: curing of polymer; high temperature materials;particle size distribution; spherulites

 

1浏览PDF格式全文需要使用软件--Abode Acrobat(由于软件较大并常见,我站不提供下载)

2、下载论文全文请点击鼠标右键“另存为”或使用断点续传软件下载(250KB)


本站收录的本文作者的其他论文

1、SKIN-CORE STRUCTURE IN MESOPHASE PITCH-BASED CARBON FIBERS: CAUSES AND PREVENTION

2、Preparation of mesocarbon microbeads from coal tar

3、用称重法研究聚丙烯腈树脂的凝固过程

 更多相关论文请点击本站的<<<站内全文搜索>>>查找

 

欢迎您参加讨论,发表您对此论文及其研究领域的看法!
(请在发言时在标题中使用所点评的论文的题目或研究方向,这样方便大家浏览!)

返回首页 | CIMS论文 | 并行工程 | 虚拟制造 | 敏捷制造 | 其他论文 | 项目开发 | 学术资源 | 站内全文搜索 | 免费论文网站大全 |

line.gif (4535 字节)

为了更好的为大家服务,欢迎您参加本站的投票调查

>>>>参加更多投票调查请点击!

本站永久域名:http://www.cimspaper.com欢迎访问

注意:本站内容未经书面允许不得转载

All rights reserved, all contents copyright 2000-2019
本站自2000年3月总网页访问量为